Green khaki fiberglass filler 200 gr - Arexons 3000
Two-component paste filler based on unsaturated polyester resins admixed with special glass fibers, which impart high mechanical properties and surface hardness to the mass.
It enables the reconstruction of small missing or badly deteriorated body parts and the filling of holes thanks to the glass fiber bridges formed over the empty spots.
Tough, medium-hard, resists water well, after curing it can be sanded.
The product can be covered with other fillers or any other finishing product.
Can also be used in the marine industry.
Fields of use
Can be applied to steel, cast iron, old paint and fiberglass without release agents.
Aluminum, light alloys, galvanized and difficult-to-adhere substrates should be treated in advance with a nonphenolic or acidic adhesion primer.
The product is not suitable for wash primers, epox primers with phenolic hardeners, thermoplastic paints, solvent-sensitive primers.
Technical characteristics
Appearance: Paste
Color: Olive green
Nature of binder: Unsaturated polyester resin
Hardener: Paste (tube)
Catalysis ratio 100 p of resin: + 1÷3 of cat
Specific gravity: 1.70 g/ml
Gel time: 6÷8 minutes
Complete polymerization: After 3 hours
Mode of use
The surface to be treated should be dry, clean, free of dust and grease, and roughened by sanding.
Rust should be removed as best as possible.
For use, add the hardener to the putty in relation to room temperature as per the following table:
| Room T° | Catalyst doses |
| Up to 10°C | 3 p. out of 100 p. (by weight) |
| 10 ÷ 20°C | 2 p. out of 100 p. (by weight) |
| Over 20°C | 1 p. out of 100 p. (by weight) |
Mix the two components until the mixture is smooth.
Apply the product with a trowel.
After 30 ÷ 40 minutes it is possible to sand.
Warnings
Application at temperatures below 10°C is not recommended.
Maximum VOC content: 250 g/l
Storage
In unopened package and stored at room temperature and out of direct sunlight 12 months.